Abstract
A new process of preparing Ti–Fe–C composites powder for reactive plasma cladding, precursor carbonization–composition process, was developed. TiC/Fe cermet coatings were synthesized by reactive plasma cladding of the composite powder. XRD and SEM were employed to analyze the phase composition and microstructure of the composite powder and coating. The hardness and wear resistance of the coating was tested. Results show that: The compound powder prepared by precursor carbonization–composition process has very tight structure, which can avert the question of raw powder breaking-up in cladding process. The TiC/Fe cermet coating by reactive plasma cladding consists of alternate, laminated layers as following: the layers in which the round nanoscale TiC particles are dispersed within the α-Fe matrix and the layers of TiC accumulation. The TiC/Fe cermet coating by reactive plasma cladding shows superior hardness and wear resistance: The surface hardness of the TiC/Fe cermet coating is 68 ± 6 (HR30 N). In the same fretting conditions, the wear resistance of Ni60 coating is twelve times than that of the TiC/Fe cermet coating.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.