Abstract
The dissimilar joining of TiAl to AISI 310 stainless steel by a reaction-assisted diffusion bonding process, using Ni/Al nanolayers as an interlayer, was investigated in the present work. The Ni and Al alternated nanolayers were deposited by d.c. magnetron sputtering onto the base materials, with a bilayer thickness of 14 nm. Joining experiments were performed at 800 °C for 60 min with compressive stress of 25 and 50 MPa. The effectiveness of the interlayer on the bonding process was assessed by microstructural characterization of the interface and by mechanical tests. Diffusion bonded joints were characterized by scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), transmission electron microscopy (TEM), high resolution transmission electron microscopy (HRTEM), scanning transmission electron microscopy (STEM) and analyzed by energy dispersive X-ray spectroscopy (EDS) in SEM and TEM and Fast Fourier Transform (FFT). The thickness of the interface region, together with its microstructural and mechanical characteristics, is affected by the use of Ni/Al multilayers; which promote joints with lower hardness values, closer to the values of the base materials, and exhibit higher shear strength.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.