Reaction sintering of fluorine-doped MgSiN 2

Abstract

Reaction bonded MgSiN 2 (RBMSN) with CaF 2 and YbF 3, as sintering additives was prepared by direct nitridation of Si/Mg 2Si/Mg/Si 3N 4 powder compact in a temperature range 1350–1550 °C. The influence of the ratio of constituents on the final phase composition, the amount of sintering additives and the influence of sintering temperature are discussed. It was shown that the starting powders should be in a ratio Mg 2Si/Mg⩾3 and Si 3N 4/Si tot⩾0.5 respectively, to obtain single-phase MgSiN 2. The oxygen content of MgSiN 2 was in the range of 0.4–0.7 wt.%. The final density of pressureless sintered RBMSN with 4 vol.% fluorine additives was 85% of theoretical density. Higher density (∼92%) was obtained for the reaction-bonded composite consisting of 48 vol.% MgSiN 2 and 52 vol.% Si 3N 4, due to the volume increase after the nitridation of silicon. The mechanical properties of fluorine-doped RBMSN were further improved by hot-pressing at 1600 °C. The 4-point bending strength and Vickers hardness (HV1) of hot-pressed materials are 427 MPa and 20.8 GPa, respectively. The indentation fracture toughness is 5.3 MPa m 1/2, due to the presence of elongated β-Si 3N 4 grains. The thermal conductivity of the dense reaction bonded MgSiN 2 is 22 W m −1K −1.