Abstract
High temperature corrosion of fuel cladding material (15-15Ti) in high burn-up situations has been an important topic for molten metal-cooled Gen-IV reactors. The present study aims to investigate the simultaneous impact of liquid lead (coolant side) and cesium molybdate (fuel side) on the cladding tube material. A capsule was designed and built for experiments between 600 °C and 1000 °C. In order to simulate a cladding breach scenario, a notch design on the cladding tube was investigated pre- and postexposure. Material thinning by corrosion and leaching at temperatures ≥ 900 °C caused breaches at the notches after 168 h exposure. The temperature dependent cladding thinning phenomenon was used for kinetic interpretation. As the first of a two-part study, this paper will focus on the exposure capsule performance, including metallographic cross-section preparation and preliminary results on the interface chemistry.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.