Abstract
AbstractChloride salts are one candidate for a >700°C concentrating solar power (CSP) cycle, however, many reports from the literature suggest very high reaction rates between chloride salts and structural alloys. Historically, a specific methodology was established for evaluating halide salt compatibility based on solution kinetics. This study returned to that paradigm where the salts are purified and evaluated in sealed capsules before moving to a flowing experiment to determine a true corrosion rate in a temperature gradient for a commercial K–Mg–Na chloride salt. Isothermal testing focused on Ni‐based alloys 230 and 600 at 600°C–800°C. The results indicated there were promising combinations of salt chemistry, temperature, and alloy composition that reduce the extent of reaction. The results of the first monometallic thermal convection loop of alloy 600 run for 1,000 hr with a peak temperature of 700°C showed low attack with rates ≤9 µm/yr.
Accepted Version (
Free)
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.