Abstract
A P, N dual-doped holey graphene (PNHG) material is prepared by a scalable, facile synthetic approach, using a mixture of glucose, dicyandiamide (DCDA), and phosphoric acid (H3PO4). H3PO4 successfully functions as an “acid catalyst” to encourage the uniform breakage of C=C bonds to create large, localized perforations over the graphene monolith. Further acid treatment and annealing introduce in-plane holes. The correlation between the capacitance of the PNHG and its structural parameters during the fabrication process is comprehensively evaluated. A thermally induced sp2→sp3 transformation occurs at high temperatures because of the substantial loss of graphitic sp2-type carbons, together with a dramatic reduction in capacitance. The target PNHG-400 electrode material delivers exceptionally high gravimetric capacitance (235.5 F g−1 at 0.5 A g−1), remarkable rate capability (84.8% at 70 A g−1), superior capacitance retention (93.2 and 92.7% at 10 and 50 A g−1 over 25000 cycles, respectively), and acceptable volumetric capacitance due to moderate density, when it is used with organic electrolytes in the voltage range between 0 and 3 V. These results suggest a pioneering defect-engineered strategy to fabricate dual-doped holey graphene with valuable structural properties for high-performance electric double layer supercapacitors, which could be used in next-generation energy storage applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.