Abstract
Nd7Fe67B22Mo3Zr1 magnets in rods have been prepared by annealing the amorphous precursors produced through injection casting. Phase formation, microstructure and magnetic properties of Nd7Fe67B22Mo3Zr1 magnets have been investigated and discussed in the as-cast and annealed states. Cast Nd7Fe67B22Mo3Zr1 rods have the soft magnetic characteristics, which changed into magnetically hard by annealing. Magnetic properties in Nd7Fe67B22Mo3Zr1 magnets are influenced by the intrinsic properties of magnetically soft α-Fe (Fe3B) and hard Nd2Fe14B phases. The Zr and Mo elements in the Nd7Fe67B22Mo3Zr1 alloy promote the formation of amorphous phase and reduce the grain size of magnetic phases. Optimal annealed Nd7Fe67B22Mo3Zr1 rods of 2mm in diameter and 52mm in length presented maximum magnetic properties such as: remanence (Br) of 0.53T, coercivity (iHc) of 1110kA/m and maximum energy product (BH)max of 49.5kJ/m3.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.