Abstract
Lithium tantalite (LiTaO3) thin films have been deposited on Pt(111)/SiO2/Si(100) substrates by means of sol–gel spin-coating technology. Using a diol-based precursor solution and rapid thermal processing (RTP), highly c-axis oriented LiTaO3 thin films are obtained and the degree of orientation is increased with an increase of the heating rate. By changing the heating rate (600–3000 °C/min) and heating temperature (500–800 °C), the effects of various processing parameters on the growth of films are investigated. With the increase of heating rate, the grain size of LiTaO3 thin films decreases markedly, and the relative dielectric constant (er) increases from 28 up to 45.6. It was found that the dielectric loss factor (cosδ) decreased, and the ferroelectric properties were improved by the increase of heating rate. The figures of merit (Fv and Fm) indicate that the LiTaO3 thin film with a heating rate of 1800 °C/min is suitable for application as a high-performance pyroelectric thin-film detector.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.