Abstract
ABSTRACTThe thermal constraints for device processing imposed by strain relaxation have been determined for a wide range of Si-Ge strained heterostructures. Misfit dislocation densities and glide velocities in uncapped Sil-xGex alloy layers, Sil-xGex single and multiple quantum wells have been measured using defect etching and TEM for a range of anneal temperatures (450°C-1000°C) and anneal times (5s-2000s). The decay of an intense photoluminescence peak (∼ 10% internal quantum efficiency ) from buried Si1-xGex strained layers has been correlated with the generation of misfit dislocations in adjacent Sil-xGex /Si interfaces. The misfit dislocation nucleation rate and glide velocity for all geometries and alloy compositions (0<x<0.25) were found to be thermally activated processes with activation energies of (2.5±0.2)eV and (2.3-0.65x)eV, respectively. The time-temperature regime available for thermal processing is mapped out as a function of dislocation density using a new kinetic model.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.