Abstract
In this work, we report rapid synthesis procedure of MIL-125 (or, Ti-BDC) Metal Organic Framework (MOF) via microwave route. The synthesized product was characterized using SEM, powder XRD, FT-IR analysis, TGA and UV–Vis diffused reflectance spectroscopy. The aim of this work was to establish a faster synthesis methodology for bulk synthesis of a potential MOF. The optimum synthesis temperature and time were found to be 120°C and 40min respectively. The variation of both microwave power and development of pressure during the synthesis conditions were closely monitored and it was observed that at optimum synthesis conditions, during the initial heating rate period, the pressure was linearly developed and reached a maximum value of ca. 14bar, however, during the holding time both the pressure and power remained fairly constant at around 6bar and 10 W respectively. The product was found photocatalytically active with a band gap energy of 3.14eV and successfully degraded methylene blue dye to ca. 96.77% in 360min.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.