Abstract
AbstractIntermetallics are known as a group of materials that draws attention with their features such as ordered structure, high temperature resistance, high hardness and low density. In this paper, it is aimed to obtain intermetallic matrix composites and also to maintain some ductile Nb and Ti metallic phase by using 99.5% purity, 35-44 μm particle size titanium, niobium and aluminium powders in one step via recently developed powder metallurgy processing technique - Electric current activated/assisted sintering system (ECAS). In this way, metallic reinforced intermetallic matrix composites were produced. Dominant phases of TiAl3 and NbAl3 which were the first compounds formed between peritectic reaction of solid titanium, niobium and molten aluminum in Ti-Al-Nb system during 10, 30 and 90 s for 2000 A current and 1.5-2.0 voltage were detected by XRD and SEM-EDS analysis. Hardness values of the test samples were measured by Vickers indentation technique and it was detected that the hardnesses of intermetallic phases as 411 HVN whereas ductile metallic phase as 120 HVN.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.