Abstract
AbstractThe rapid solidification experiments have been carried out for the Nb(45‐x)YxNi55 (x = 9, 19, and 27) alloys. The microstructure characterization shows the occurrence of the liquid‐liquid phase separation into the Niobium‐rich and Yttrium‐rich liquids. The Niobium‐rich spherical particles were embedded in the glassy Yttrium‐rich matrix for the alloy Nb36Y9Ni55, while glassy Yttrium‐rich ones were located in the glassy Niobium‐rich matrix for the alloy Nb18Y27Ni55. A structure of hierarchical separation was detected in the as‐quenched alloy Nb26Y19Ni55. The size distribution of the spherical particles in the as‐quenched Nb(45‐x)YxNi55 (x = 9 and 27) alloys ranges from several nanometers to sub micrometer and is close to the Gaussian distribution. The average diameters of the Niobium‐rich particles in the as‐quenched Nb36Y9Ni55 alloy and the Yttrium‐rich particles in the Nb18Y27Ni55 alloy are 0.23 μm and 0.15 μm, respectively. A dual‐glass structure in the as‐quenched Nb18Y27Ni55 alloy ribbon was determined by X‐ray diffraction and transmission electron microscopy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.