Abstract
AbstractWe report on a rapid sintering protocol, which optimizes the preparation of 0‐29 mol% Gd‐doped ceria ceramics with density ≥98% of the theoretical crystal lattice value. The starting material is a nanometer grain‐sized powder prepared by carbonate co‐precipitation and calcined with minimal agglomeration and loss of surface area. Slow (5°C/min) heating of the green‐body from 500°C to the optimum temperature of rapid sintering (, dwell time <1 minute) followed by 20°C/min cooling to 1150°C with 6 minutes dwell time, produces maximum pellet density. increases from 1300 to ~1500°C with increase in Gd‐content, while the average grain size in the maximally dense pellets, as determined by scanning electron microscopy, ranges between 600 nm and ~1 μm. For each doping level, the logarithm of the average grain size decreases linearly with 1/T1. By avoiding extended exposure to sintering temperatures, this protocol is expected to minimize undesirable Gd segregation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.