Abstract
Micro-, submicron-, and nano-scale titanium dioxide particles were reduced by reduction with a metallic calcium reductant in calcium chloride molten salt at 1173K, and the reduction mechanism of the oxides by the calcium reductant was explored. These oxide particles, metallic calcium as a reducing agent, and calcium chloride as a molten salt were placed in a titanium crucible and heated under an argon atmosphere. Titanium dioxide was reduced to metallic titanium through a calcium titanate and lower titanium oxide, and the materials were sintered together to form a micro-porous titanium structure in molten salt at high temperature. The reduction rate of titanium dioxide was observed to increase with decreasing particle size; accordingly, the residual oxygen content in the reduced titanium decreases. The obtained micro-porous titanium appeared dark gray in color because of its low surface reflection. Micro-porous metallic titanium with a low oxygen content (0.42wt%) and a large surface area (1.794m2g−1) can be successfully obtained by reduction under optimal conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.