Porous polymeric films are promising materials for the production of ultralow-dielectric constant materials. A high porosity polyimide thin film was prepared via the phase separation of a polyimide precursor in an N,N-dimethylacetamide (solvent)/2-(diethylamino)ethyl methacrylate/photoinitiator system. A novel technique involving high-pressure CO2 (5 MPa) gas injection was used to form CO2-2-(diethylamino)ethyl methacrylate zwitterion salt and induce the immediate phase separation and solvent droplet formation (within 60 s) of a wet precursor film on a metal substrate. The film was exposed to UV light through quartz windows for 30 s to polymerize the 2-(diethylamino)ethyl methacrylate while maintaining a constant CO2 pressure. The cured thin film containing numerous pores with an average diameter of approximately 1 μm ± 1.0 μm was treated at 320 °C for 1 h under a continuous flow of nitrogen. The obtained film was 30 μm thick and exhibited pores with an average diameter of approximately 1 μm ± 0.9 μm. The...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.