Abstract
This work shows for the first time the possibility to sinter BCZT powder compacts by rapid heating rates within one hour of sintering, while achieving good piezoelectric properties. The sintering was performed by rapid (heating rates 100 and 200 °C/min) pressure-less sintering (PLS) at 1550 °C/5-60 min and by SPS sintering (100 °C/min, 1450 °C/5−60 min and 1500 °C/15−45 min). The rapid PLS samples reached a relative density up to 94 % and grain sizes of 17–36 μm acquiring d33 up to 414 pC/N. Although the SPS samples reached full density at 1450 °C, their piezoelectric properties worsened due to smaller grains (10−15 μm) as well as formation of cracks at dwell times > 30 min. At elevated SPS temperature of 1500 °C/30 min, the d33 increased to 360 pC/N sustaining full density. Even higher increase in d33 (424 pC/N) of SPS samples was achieved by post-rapid PLS at 1550 °C/60 min resulting from further expansion in grain size.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.