Abstract
ABSTRACTPorous Ni3Al, NiAl, and NiAl3 intermetallics have been synthesized through simple and rapid process of thermal explosion (TE) from 75 at.% Ni/25 at.% Al, 50 at.% Ni/50 at.% Al and 25 at.% Ni/75 at.% Al elemental powders. The effect of the three components on temperature profile, phase composition, pore structure, and oxidation resistance were investigated. The results showed that the temperature of the specimens increased rapidly from 638°C to 1381°C, 620°C to 1613°C and 642°C to 1172°C in a few seconds. X-ray diffraction patterns indicated that Ni3Al, NiAl, and NiAl3 were the main phase or single-phase compounds in the TE products. Porous Ni3Al, NiAl, and NiAl3 intermetallics showed variable pore structures. Moreover, all the products of three components exhibited good oxidation resistance, particularly the porous NiAl and NiAl3 intermetallics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.