Abstract
Rapid dendritic growth in undercooled liquid Ni80Cu10Co10 alloy has been investigated. This liquid ternary alloy was undercooled by a large degree up to 335 K(0.2TL) with electromagnetic levitation method. The rapidly solidified microstructure is revealed to be α-Ni solid solution phase by X-ray diffraction and differential scanning calorimetry. With the increase of undercooling, the microstructure is drastically refined. Its morphology transfers from coarse dendrite into equiaxial grains when undercooling exceeds 110 K. The solute microsegregation is suppressed with the enhancement of solute trapping effect under high undercooling condition. The dendritic growth velocity was measured as a function of undercooling. At extremely large undercoolings, the dendritic growth velocity of α-Ni phase is restrained by the solute diffusion of Cu and Co, and even decreases once undercooling exceeds 284 K.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.