Abstract
Doping lithium (Li) and/or nitrogen (N) in ZnO and activation of shallow acceptors thereby have drawn specific scientific interest for the last few years. A comprehensive study employing Raman spectroscopy is being reported here on N and Li implantation effects in ZnO. Strong presence of 275 cm−1 Raman mode after N and (Li,N) implantation confirms its relation with doped nitrogen in ZnO. Weak presence of 510 cm−1 mode in the high fluence implanted ZnO indicates its origin with interstitial defects. No extra Raman mode has been identified in Li implanted samples. Raman mode with anomalously large intensity is found at 1562 cm−1 after (Li,N) co-implantation (highest fluence). Implantation causes huge increase of Raman modes ~ 540, 555 and 579 cm−1, with the last two bearing clear co-relations with interstitial Zn and O vacancy, respectively. To identify shallow acceptors due to dopant-defect complex, low temperature photoluminescence (PL) has been monitored but only donor related excitonic features are visible in the near band edge (NBE) emission. However, indications in favour of deep acceptors states are noted, particularly when Li is present in the sample. The deep acceptor level may be at~ 300 meV above the valence band consistent with previous results.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.