Abstract
Expitaxial layers of ZnSxSe1 − x were grown on GaAs(100) at room temperature by molecular beam epitaxy (MBE) using compound sources for the evaporation of both ZnSe and ZnS. The formation of the ternary compound was monitored on-line by taking Raman spectra from the sample surface, i.e. continuously during the growth process. The spectra display ZnSxSe1 − x-related scattering processes up to third order under resonant excitation using the 2.808 eV (441.6 nm) emission line of a HeCd laser. From the frequency positions of the ZnSe- and ZnS-like longitudinal optical (LO) phonon modes the sulfur content x was determined. The Raman scattering intensity displays a characteristic modulation upon deposition time due to Fabry-Perot interference of the incident as well as the scattered light. From the period of this modulation, the growth rate was calculated. Furthermore, photoluminescence (PL) spectra were taken in situ using the 3.81 eV (325 nm) emission line of the HeCd laser. They display the near band edge emission of the ZnSxSe1 − x layer in the blue spectral region.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.