Radiation Induced Segregation at Grain Boundary in an Austenitic Stainless Steel under Ion Irradiation.

Abstract

Chromium depletion near grain boundaries of austenitic stainless steel during irradiation was investigated. Specimens were kept at 1,473 K for 30 min, and were quenched into the water. Irradiations were done using 400 keV He+ ions at 573, 673 and 773 K up to 10dpa with a dose rate of 2.4×10−4 dpa/s. After irradiation, the Cr concentration profile near the grain boundary was measured using an analytical electron microscope with a 1 nm beam diameter. At 573 K, Cr depletion is small, and its concentration at the grain boundary decreases to 15.5 mass% at 3 dpa from the initial concentration of 18.5 mass%. At 673 and 773 K, Cr concentration at the grain boundary rapidly decreases between 0 and 0.2dpa, and then gradually approaches a constant value, 7.0 mass% at 673 K and 5.0 mass% at 773 K. Two stages are found in radiation induced segregation (RIS) behavior, one stage in which Cr depletion and Ni enrichment balance and another in which Fe depletion and Ni enrichment balance. These experimental results were co...