Abstract
The purpose of the present article is to develop a multi-scale brittle fracture modelling for irradiated RPV materials. For this development, applicability of local brittle fracture criteria for radiation embrittlement modelling is analysed through comparison of the predicted and test results on radiation embrittlement of RPV steels in terms of ductile-to-brittle transition temperature and fracture toughness. The influence of radiation-induced defects on the processes of cleavage microcrack nucleation and propagation is clarified. The physical-and-mechanical models of the effect of irradiation-induced defects on cleavage microcrack nucleation are developed on the basis of dislocation and brittle fracture theories. Stress-and-strain controlled fracture criterion is developed that allows the adequate prediction of radiation embrittlement by various mechanisms. The differences and commonalities are revealed in the nature of material embrittlement due to cold work and neutron irradiation. The mechanism is explained of significant recovery of fracture resistance properties with simultaneous increase of fraction of intercrystalline fracture after post-irradiation annealing. Engineering approach for prediction of the temperature dependence of fracture toughness as a function of neutron fluence is justified.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.