Radiation crosslinking and sorption properties of hydrogels based on 1‐vinyl‐2‐pyrrolidone, hydroxyethyl methacrylate, and their copolymers

Abstract

AbstractThis work has been concerned with the synthesis of the hydrogels of poly (vinyl pyrrolidone) (NVP), poly (hydroxy ethylmethacrylate) (HEMA), and their copolymer under the effect of gamma radiation in the presence of N,N‐methylenebisacryl‐amide (MBAm) as a crosslinking agent. The effect of the different factors that may affect the gelation and yield product, such as solvent composition and irradiation dose, was investigated. The formed hydrogels were characterized in terms of swelling in water and different organic solvents, X‐ray diffraction (XRD), and IR spectroscopic analysis. The sorption capability of these hydrogels towards some commercial basic and acid dyesstuffs was also studied. The results showed that a solvent mixture composed of equal contents of water and methanol is the most suitable to afford the minimum sol fraction and the highest yield product at a minimal irradiation dose of 10 kGy. It was observed that NVP hydrogel displayed the highest swelling in water, alcohols, and dimethyformamide of ∼1300% and a lower tendency to swell in nonpolar solvents. The results showed that HEMA hydrogel has a high affinity to absorb basic dyes while NVP has a tendency for acid dyes. Also, the sorption of either the basic or acid dyes by the different hydrogels was found to greatly depend on the concentration of dye in solution and the mass of the used hydrogel. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 91: 3274–3280, 2004