Abstract
Abstract In this paper, the results of a study aimed at understanding the extrinsic influence of test specimen orientation, with respect to a wrought alloy-steel plate, on the stress-controlled cyclic fatigue properties and fracture behavior of a structural steel is highlighted. The alloy steel chosen was ASTM A572 grade 50. Samples of this alloy steel, prepared from both the longitudinal and transverse orientations, were cyclically deformed over a range of maximum stress and the corresponding number of cycles to failure (NF) was recorded. The influence of test specimen orientation and intrinsic microstructural effects on cyclic fatigue life and fracture behavior are presented and discussed. Overall, the macroscopic fracture mode was essentially identical regardless of orientation of the test specimen with respect to the wrought plate. The microscopic mechanisms governing cyclic deformation, fatigue life, and final fracture behavior are presented in light of the mutually interactive influences of magnitude of applied stress, intrinsic microstructural effects, orientation of test specimen, and deformation characteristics of the key microstructural constituents.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.