Abstract
In this work, the correlation between different microstructural components and hydrogen trapping with high density in tempered niobium carbide (NbC)-precipitated martensitic steel was quantitatively investigated using a combination of electrochemical hydrogen permeation experiments and thermal desorption spectroscopy. The martensite lath and a high density of dislocations, which constitute the reversible hydrogen trapping sites, with a density of 2.24 × 1020 cm−3 in Fe-0.05C-1.10Mn-4.50Ni-0.50Cr-0.50Mo-0.05Nb wt.% martensitic steel. The dislocation with high density could disperse the hydrogen distribution. Furthermore, the uniformly distributed NbC nanoprecipitates, the high-angle grain boundaries, and the grain-boundary precipitates were found to act as irreversible hydrogen traps, with a density of 1.00 × 1020 cm−3. These deep hydrogen trapping sites could not only trap hydrogen irreversibly, but also can inhibit the accumulation of hydrogen. The interpretation of hydrogen trapping is significant to enhance the hydrogen embrittlement resistance of high-strength martensitic steels.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.