Abstract
Using a fatigue testing method by which fatigue cracks can be initiated and propagated in a film adhered to cover a circular through-hole in a base plate subjected to pull-pull cyclic loads, annealed rolled pure copper films of 100μm thickness were fatigued. In order to discuss about the correlation between fatigue crack propagation and the change of crystal orientation, crystal orientation on the surface of the film materials was measured before and after fatigue testing. The crystallo-graphic information of these films was analyzed using the EBSD (Electron Back-scatter Diffraction) system and the quantitative evaluation method for the crystal rotation angle, the rotation axis and the rotation direction with fatigue testing was developed based on the analysis of crystal orientation matrix. As a result, the crystal rotation angle near the fatigue crack is larger than that apart from the crack and the crystal rotation was quantitatively larger around the transgranular crack than the intergranular crack propagated along the annealing twin boundary.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.