Abstract
In this paper, a centrifuge device is proposed to facilitate the intrusion of a low-melting point metal alloy into the pore space of hardened cement paste. X-ray microtomography is combined with metal centrifugation porosimetry (MCP) to quantitatively investigate 3D pore structure. The low-melting-point metal alloy is melted and introduced into pore space in pastes with water cement ratio of 0.5 and 1.0 at a temperature of 65 °C. 3D pore structure is quantitatively analyzed by X-ray microtomography after the molten metal alloy has been consolidated. A new threshold value segmentation method for pore space was proposed using conversion coefficient on region of interest (ROI). Porosity and pore size distribution are tested by MCP and compared with the results based on mercury intrusion porosimetry (MIP). The results show that the contrast between pore space and solid phase in the X-ray microtomography device image is improved. The total porosity obtained by MCP was found to be consistent with the results obtained by MIP.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.