Quantitative analysis of the Ge concentration in a SiGe quantum well: comparison of low-energy RBS and SIMS measurements

Abstract

The germanium concentration and the position and thickness of the quantum well in molecular beam epitaxy (MBE)-grown SiGe were quantitatively analyzed via low-energy Rutherford backscattering (RBS) and secondary ion mass spectrometry (SIMS). In these samples, the concentrations of Si and Ge were assumed to be constant, except for the quantum well, where the germanium concentration was lower. The thickness of the analyzed quantum well was about 12 nm and it was situated at a depth of about 60 nm below the surface. A dip showed up in the RBS spectra due to the lower germanium concentration in the quantum well, and this was evaluated. Good depth resolution was required in order to obtain quantitative results, and this was obtained by choosing a primary energy of 500 keV and a tilt angle of 51 degrees with respect to the surface normal. Quantitative information was deduced from the raw data by comparing it with SIMNRA simulated spectra. The SIMS measurements were performed with oxygen primary ions. Given the response function of the SIMS instrument (the SIMS depth profile of the germanium delta (delta) layer), and using the forward convolution (point-to-point convolution) model, it is possible to determine the germanium concentration and the thickness of the analyzed quantum well from the raw SIMS data. The aim of this work was to compare the results obtained via RBS and SIMS and to show their potential for use in the semiconductor and microelectronics industry. The detection of trace elements (here the doping element antimony) that could not be evaluated with RBS in low-energy mode is also demonstrated using SIMS instead.