A new Sr2Si1−xAlxO4−x/2☐x/2 (x=0, 0.028, 0.06 and 0.075) silicate series has been prepared and the structural and electrical properties were investigated. These samples present three different polymorphs (β, α′L and α′H) and the increase of Al-content resulted in a shift of the polymorph content, from a monoclinic form to an orthorhombic one. Aluminium contents higher than x=0.06 did not lead to any further change in the ratio of polymorphs. High temperature X-ray diffraction studies showed a complete stabilisation of α′L, presenting a superstructure orthorhombic form, at temperatures between RT and 250 °C. At temperatures higher than 500 °C a basic orthorhombic cell is stabilised. Thermogravimetric analysis displayed an increase of the water uptake on doping, due to the generation of oxide vacancies in the lattice. Electrical characterisation in dry and wet atmospheres showed an important proton contribution to the conductivity. In addition, measurements in N2 and O2 fluxes displayed a significant p-type electronic contribution to the overall conductivity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.