Qualitative observations on the diffusion of copper and gold through a nickel barrier

Abstract

To retard failure of gold plated copper parts by diffusion of copper to the gold surface, a layer of nickel is frequently used between the copper and gold as a diffusion barrier. To evaluate the mechanisms whereby the nickel retards the motion of copper atoms to the gold surface, planar tri-couples of Cu/Ni/Au were prepared by electroplating nickel and gold layers on OFHC copper coupons. Diffusion anneals were carried out at temperatures from 150 to 750°C. A qualitative evaluation of diffusion behavior was provided by an electron microprobe utilizing X-ray wavelength dispersive analysis on polished cross sections. Results demonstrate that the nickel layer retards but does not block the transport of copper to the gold surface. Possible mechanisms for the anomalous buildup of copper at the gold/nickel interface and gold at the copper/nickel interface are discussed.