Abstract
The preparation of thermo-crosslinking hydrogel fibers composed of poly(vinyl alcohol) (PVA) and poly(acrylic acid) (PAA) was presented. The hydrogel fiber was prepared by extruding the spinning dope from in situ polymerization of acrylic acid in the presence of PVA into coagulating bath of saturated ammonium sulfate aqueous solution. The network was formed by thermally heating the dried fibers under vacuum. The final hydrogel fibers exhibit pH-sensitive behavior and show hysteresis loop in the pH range from 2.5 to 12.5. The pH value at which the swelling ratio of the fiber had a jump shifted to lower value with increasing the PAA content within the network. Increasing the heating temperature and time for the fibers, the swelling ratio decreased and the jump point pH shifted to higher pH value. The oscillatory swelling/contracting behavior of the hydrogel fiber exhibited a well reversible pH-responsive property.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.