Push-out Bond Strength of RealSeal SE and AH Plus after Using Different Irrigation Solutions

Abstract

IntroductionThe aim of this investigation was to evaluate the influence of different endodontic irrigants (sodium hypochlorite [NaOCl], chlorhexidine [CHX], and EDTA) on the push-out bond strength of the obturation materials RealSeal SE (SybronEndo, Orange, CA) and AH Plus (Dentsply International Inc, York, PA). MethodsTwo hundred human root canals were prepared and divided into 2 groups according to the filling material (RealSeal SE vs AH Plus). Each group was subdivided into 5 groups according to the irrigation protocol (0.9% saline [control], 3% NaOCl, 3% NaOCl with saline, 17% EDTA, and 2% CHX). After obturation, roots were sliced into 1-mm discs for push-out assessment. Compressive loading was performed using an universal testing machine at a speed of 0.5 mm/min. Two-way analysis of variance and the Kruskal-Wallis test were performed for pair-wise comparisons to assess the differences between the experimental groups. ResultsAH Plus exhibited a significantly higher bond strength than RealSeal SE (mean = 2.53 and 1.53 MPa, respectively; P < .05), except with saline alone (P > .05). Within the AH Plus groups, no significant differences existed between the irrigants and saline alone (P > .05). The bond strength of RealSeal SE with saline alone or with NaOCl and saline did not differ from that of AH Plus with saline alone (P > .05). However, the push-out bond strength of RealSeal SE decreased by approximately half (P < .05 compared with RealSeal SE with saline alone) after rinsing with NaOCl alone, EDTA, or CHX. ConclusionsThe bond strength of RealSeal SE is highly influenced by the irrigant used.