Abstract
Room temperature (RT) pulsed operation of blue (420 nm) nitride based multi-quantum well (MQW) laser diodes grown on a-plane and c-plane sapphire substrates has been demonstrated. A combination of atmospheric and low pressure metal organic chemical vapor deposition (MOCVD) using a modified two-flow horizontal reactor was employed. The emission is strongly TE polarized and has a sharp transition in the far field pattern above threshold. Threshold current densities as low as 12.6 kA/cm 2 were observed for 10 X 1200 micrometer lasers with uncoated reactive ion etched (RIE) facets on c-plane sapphire. Cleaved facet lasers were also demonstrated with similar performance on a-plane sapphire. Differential efficiencies as high as 7% and output powers up to 77 mW were observed. Laser diodes tested under pulsed conditions operated up to 6 hours at room temperature. Performance was limited by resistive heating during the electrical pulses. Lasing was achieved up to 95 degrees Celsius and up to a 150 ns pulse length (RT). Threshold current increased with temperature with a characteristic temperature, T 0 , of 125 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.