Abstract
Based on the welding require of Hastelloy C-276 in the industry, the pulsed laser welding of 0.5 mm thickness Hastelloy C-276 was investigated, and the smooth weld joint with refined grain was obtained. Then, the defect in the weld joint was tested by the X-Ray flaw detection and micro-examination, and the corrosion-resistant property of weld joint was evaluated via the strong acid and electrochemistry corrosion. By the X-Ray flaw detection, there were not obvious defects in the weld joint, and just two micro-pores were found during the micro-examination. In addition, the corrosion-resistant property of the weld joint in the strong acid corrosion was nearly the same as that of the base metal. The polarization curve in the weld joint, resulted from the electrochemistry corrosion test, was found a little difference from that of base metal. The results indicated, for the thin Hastelloy C-276 sheet, using the pulsed laser welding could obtain the well weld joint with little defect, and the corrosion-resistant property was impacted by the pulsed laser welding process.Based on the welding require of Hastelloy C-276 in the industry, the pulsed laser welding of 0.5 mm thickness Hastelloy C-276 was investigated, and the smooth weld joint with refined grain was obtained. Then, the defect in the weld joint was tested by the X-Ray flaw detection and micro-examination, and the corrosion-resistant property of weld joint was evaluated via the strong acid and electrochemistry corrosion. By the X-Ray flaw detection, there were not obvious defects in the weld joint, and just two micro-pores were found during the micro-examination. In addition, the corrosion-resistant property of the weld joint in the strong acid corrosion was nearly the same as that of the base metal. The polarization curve in the weld joint, resulted from the electrochemistry corrosion test, was found a little difference from that of base metal. The results indicated, for the thin Hastelloy C-276 sheet, using the pulsed laser welding could obtain the well weld joint with little defect, and the corrosion-resistant...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.