Pulsed laser deposition of oxide gate dielectrics for pentacene organic field-effect transistors

Abstract

We have fabricated Al 2O 3, LaAlO 3 (LAO), CaHfO 3 (CHO) and CaZrO 3 (CZO) thin films for the dielectric layers of field-effect transistors (FETs) by pulsed laser deposition (PLD). The films exhibited very smooth surfaces with root-mean-squares (rms) roughnesses of ∼1.3 Å as evaluated by using atomic force microscopy (AFM). The breakdown electric fields of Al 2O 3, LAO, CHO and CZO films were 7, 6, 10 and 2 MV/cm, respectively. The magnitude of the leak current in each film was low enough to operate FET. We performed a comparative study of pentacene FET fabricated using these oxide dielectrics as gate insulators. High field-effect mobility of 1.4 cm 2/V s and on/off current ratio of 10 7 were obtained in the pentacene FET using LAO gate insulating film. Use of the LAO films as gate dielectrics has been found to suppress the hysteresis of pentacene FET operations. The LAO films are relevant to the dielectric layer of organic FETs.