Abstract
ABSTRACTThe structure, morphology, and electrical properties of pulsed laser deposited NbNx (0 ≤ x ≤ 1.4) thin films have been investigated. Films were deposited from Nb metal targets on oriented MgO (100) and amorphous fused silica substrates as a function of substrate temperature and ambient pressure. A reducing atmosphere (N2 with 10% H2) was used to prevent oxide formation. At elevated temperatures, the N/Nb ratios of films deposited on MgO, as determined from Rutherford Backscattering Spectroscopy, increased from 0 −1.4 as the ambient pressure was varied from vacuum to 200 mTorr, respectively. NbNx films (x=l) were deposited at 600 °C and 60 mTorr. Both the structure and electrical properties of the deposited films varied strongly with the substrate type. On fused silica, NbN films were poorly crystalline with low critical temperatures (Tc ∼ 8 – 11 K) and low critical currents (Jc (4.2 K) ∼ 2 MA/cm2), whereas on MgO the NbN films were oriented and had better transport properties (Tc ∼ 16.4 K and Jc (4.2 K) = 7.1 MA/cm2).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.