Abstract
Effect of re-annealing treatment in thermoluminescence response of thermoluminescent dosimeter (TLD) CaSO4:Dy and CaSO4:Dy with PTFE (Polytetrafluoroethylene) addition was investigated. CaSO4:Dy was prepared by a co-precipitation method. The PTFE was added before re-annealing treatment which the mass ratio of CaSO4:Dy and PTFE was fixed to 2:3. The re-annealing treatments of the samples were done at temperature 700 °C for 1 hr. The obtained samples were characterized using a Fourier-transform infrared (FTIR) and X-ray diffraction (XRD) to observe the molecule bonding in sample and crystal properties, respectively. From the experimental results, it was observed that the thermoluminescence intensity of CaSO4:Dy, CaSO4:Dy re-annealed at 700 °C, and CaSO4:Dy + PTFE re-annealed at 700 °C are 57.03, 75.15, and 1191.11 nC, respectively. The intensity of 700 °C-re-annealed CaSO4:Dy increased significantly after PTFE addition.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.