Abstract
Noble metals are added to boiling water reactors (BWRs) to mitigate stress corrosion cracking of structural components made from steels and Ni-based alloys and this technology is referred to as Noble Metal Chemical Addition (NMCA) or NobleChemTM. There is a growing concern that NMCA can cause unwanted harmful effects on the corrosion and hydrogen uptake properties of Zircaloy-2 fuel cladding. To investigate this, we have subjected Zircaloy-2 fuel claddings to out-of-pile BWR conditions in a custom-built autoclave. These claddings are oxidized in pressurized hot water (280 °C, 9 MPa) for 25, 60 and 150 days, wherein Pt nanoparticles (~10 nm) were simultaneously injected. Cross-sectional focused ion beam cuts made at the oxide-metal interface reveal that the oxide growth is not significantly influenced by the local Pt loadings (≤ 1 µg·cm-2). Surprisingly, an inverse correlation was observed between oxide thicknesses and metal's hydrogen contents. Interestingly, Pt catalysts have led to diminished hydrogen absorption in specimens with liner exposed to the hot water. Overall, Pt catalysts exhibited no detrimental effects on the corrosion rate and hydrogen absorption in Zircaloy-2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.