Abstract
The oxidation behavior of AlCrN coating deposited on Ti-25Al-12.5Nb-6Mo-0.48V alloy was investigated at 700 °C and 800 °C in static air. Oxidation in air indicated that the uncoated alloy exhibited poor oxidation resistance due to the formation of TiO2 scale, but the major oxide in the oxidized coating was chromia and alumina and the TiN layers were also observed beneath the coating. No sign of degradation and no scaling of the coating was observed after oxidation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.