Abstract
The objective of the present work is the evaluation of a proposal for a gapped bead-on-plate (G-BOP) test, used for study of hydrogen cracks in relatively thin sheets of welded steel. That new proposal consists of the replacement of the usual solid blocks by an assembly of blocks in such a way that the test can evaluate weld beads on thin sheets. Student t distribution is applied to examine the functionality of the proposed test. Weld metals were deposited with flux-cored wires E71T-1 and E71T8-K6, with diameters of 1.6 and 1.7 mm, respectively, under two different preheating temperatures. Metal susceptibility to hydrogen cracking was evaluated by the presence and percentage of cracks in the weld metal. In order to evaluate and verify the functionality of the new G-BOP test proposal, the following were examined: efficiency of the new test in inducing hydrogen cracks in the weld metal, result replicability, fracture modes present in cracks, and the cooling rate imposed on the welding zone. Results showed that the new G-BOP test proposal is viable; results were replicable and the test was efficient in inducing cracks in weld metal with a confidence of 90%.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.