Abstract
Water blown rigid polyurethane foams with different functionality were prepared. The physical properties of rigid foams were measured with rotational viscometer (NDJ-1), universal testing machine (Instron3365), scanning electron microscope (SEM) and differential scanning calorimeter (DSC). The results show that the viscosity of polyether polyol increases exponentially from 62 mPa s to 6 000 mPa s with the increase of functionality from 2 to 5.6, respectively. The overall density of foam increases slightly from 31.7 kg/m(3) to 37.4 kg/m(3) with increasing functionality while core density exhibited little difference. Compressive strength of foam shows the similar behavior wit h density except for 2-functional sample. At the same time, dimensional stability becomes better with increasing functionality except for 5.6-functional foam that has worse stability than 4.8-functional foam. From the SEM results, the functionality is not an important factor in determining distribution of cell size of foam. According to the results of thermal analysis, the glass transition temperature (T-g) shifts to a higher temperature from 128.9 degrees C to 166.3 degrees C for the 2 to 5.6 functional foam, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.