Abstract
We have investigated the effects of film thickness, anti-reflective (AR) coating and surface roughness on the optical transparency of silicon carbide (SiC) membrane. Peak transmittances monotonously increased as the thickness decreased. The transmittance at 633 nm for 1.05 micrometers thick SiC membrane adjusted by reactive ion etching was 70%, and increased up to 80% by an AR coating. SiC membrane with extremely smooth surface of 0.12 nm (Ra) has been obtained by polishing, and had peak transmittances of 69% and 80% at 633 nm for 2.0 micrometers and 1.0 micrometers in thickness, respectively. Poly-crystalline (beta) -SiC membrane in the suitable tensile stress range of 0.3 to 2.0 X 10<SUP>8</SUP> Pa and with high Young's modulus of 4.5 X 10<SUP>11</SUP> Pa has been prepared by a hot wall type low pressure chemical vapor deposition, and been found to need to have thickness over 0.7 micrometers to maintain sufficient mechanical strength in processing.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.