Abstract
To improve the mechanical properties of poly(vinyl chloride) (PVC), the characters of combining PVC with elastomers were considered. Polybutadiene grafted poly(methyl methacrylate) (PB-g-PMMA, MB) core-shell particles were prepared by emulsion polymerization, and were used as an impact modifier for PVC. The impact resistance, fracture, brittle-ductile transition and the morphology of PVC/MB blends were investigated. It was found that MB particles had a high toughening efficiency for PVC resin, the impact strength was more than 1100 J·m-1 when MB was 8 phr. Two factors influence the impact strength and brittle-ductile transition, one is the modifier content, and the other is core-shell weight ratio. The impact curves are Ω-like shape, the impact strength value is the highest at the middle part and the PVC/ MB blends show ductile break behaviors. The core shell ratio of ductile areas are limited from 80/20 to 90/10 for PVC/MB=100/8, and 70/30 to 93/7 for PVC/MB=100/10.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.