Abstract
AbstractA series of Ga2O3‐based (Inx Ga1–x )2O3 alloy thin films have been grown on c‐plane sapphire substrates with a thin Ga2O3 buffer layer by plasma‐assisted molecular beam epitaxy. At growth temperatures of 700 °C and higher, even with a slight inclusion of In2O3 to Ga2O3, for example, the film of (In0.08Ga0.92)2O3, exhibited a rough surface and degraded transmission spectrum resulting from phase separation of In2O3. Due to low temperature growth at 600 °C, however, the phase separation was suppressed for the In composition up to 35%, which was confirmed by X‐ray diffraction measurement, and the films exhibited high transmittance over 85% with sharp absorption edges. The bandgap could be tuned form 5.0 to 4.0 eV. The results encourage the application of (Inx Ga1–x )2O3 thin films in short‐wavelength optical devices. (© 2008 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.