Abstract
Physical and mechanical properties were evaluated for bamboo-oriented strand boards (BOSB) prepared with combinations of two contrasting bamboo species and bonded with phenol formaldehyde resin under various compression ratios. The strands from the culms of Gigantochloa pseudoarundinacea and Dendrocalamus asper bamboo were steam-treated at a temperature of 126 °C and a pressure of 0.14 MPa for 1 h and then washed with a 1% NaOH solution. Three-layer dual-species bamboo-oriented strand boards with a shelling ratio of 25 to 50 to 25 (face to core to back) were manufactured with different compression ratios using an 8% phenol formaldehyde adhesive and 1% paraffin. The slenderness ratio and aspect ratio were evaluated by measuring 100 random strands to determine uniformity. The solidity profiles of the dual-species bamboo-oriented strand boards (thickness direction) were relatively uniform. The modulus of rupture, modulus of elasticity, and internal bond values of the dual-species bamboo-oriented strand boards increased as the compression ratio increased, but the water absorption and thickness swelling decreased. The dual-species bamboo-oriented strand boards prepared with compression ratios of 1.44 to 1.25 and 1.54 to 1.33 met all the requirements of CSA standard 0437 (2011). The optimum compression ratio for the preparation of dual-species bamboo-oriented strand boards was 1.44 to 1.25.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.