Abstract
This article investigates the effects of stone powder sludge on the microstructure and strength development of alkali-activated fly ash and blast furnace slag mixes. Stone powder sludge produced from a crushed aggregate factory was used to replace fly ash and granulated blast furnace slag at replacement ratios of 0%, 10%, 20%, and 30% by mass. The unit weight and compressive strength of the samples were measured, and scanning electron microscopy/energy dispersive spectroscopy and X-ray diffraction (XRD) analyses were performed. The test results indicated that the compressive strength of alkali-activated blast furnace slag mixes using stone powder sludge was higher than that of the alkali-activated blast furnace slag control mix, but the compressive strength of alkali-activated fly ash mixes decreased with increasing replacement ratio of stone powder sludge. Microscopy results indicated that for alkaliactivated blast furnace slag samples, broken surfaces were more evident than for the alkali-activated fly ash samples. For all XRD diagrams, broad and diffuse peaks were observed around 2θ = 35° (d = 2.96–3.03 A), implying amorphous or short-ordering structure phases.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.