Abstract
Non-hydrogenated amorphous Silicon-Germanium (a-SiGe) thin films were deposited at two different base pressures by RF magnetron co-sputtering. Moreover, an ex-situ thermal annealing was carried out to investigate the material properties to be suitable as the bottom cell of multi-junction solar cells. Compositional study of the films using EDX showed Ge-rich thin films with 75 atomic% of Ge. XRD reflection study implied that all samples were entirely amorphous in nature. However, a significant improvement of morphology possibly due to low base pressure was observed while thermal annealing caused peening and reduction of surface inhomogeneity in both as-sputtered films. UV-VIS-IR analysis confirmed the FESEM results. The highest transmittance was observed in the as-deposited sample grown at 4 x 10(-5) Torr, which however reduced after thermal annealing. Tauc's model was implied for band gap determination and band gap energy as low as 1.07 eV was found in the annealed sample grown at lower base pressure (4 x 10(-6) Torr). Electrical properties of films were investigated by Hall effect measurement system and results found the reduction of resistivity with the same trend of optical band gap energy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.