Abstract
Yttria stabilized zirconia materials are frequently used in mechanical engineering and biomedical applications. Demanding loading conditions require materials combining a high level of strength and fracture toughness. A ready-to-press alumina doped 2 mol% yttria-stabilized zirconia powder was shaped by axial pressing and sintering in air at 1250–1500 °C for 2 h. At 1350 °C the best combination of strength (1450 MPa) and toughness (7.8 MPa√m) was achieved. Materials sintered in the middle of the chosen temperature range combine full density, high transformability and small grain size. Toughness measurements by direct crack length measurements delivered unrealistically high fracture toughness values.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.