Properties dependence of the lightweight alumina products obtained by a semi-dry pressing method on the alumina type

Abstract

Lightweight materials are widely used in industry for thermal insulation of various thermal units. The choice of lightweight material depends on the specific conditions of service. For the lining of high-temperature units operating in reducing environments, alumina lightweight products are used that contain a minimum amount of Fe2O3 impurities and free (unbound in compounds) SiO2.
 In JSC “URIR named after A. S. Berezhnoy” a technology of alumina lightweight products of grades KLA-1.1 and KLA-1.3 by a semi-dry pressing method with an application temperature of up to 1550 °C has been developed. These products are made from a mixture of ground and no-milled γ-form alumina of grade 0 and α-form alumina of grade S with additives of pitch coke and chalk.
 The work purpose was improvement of the alumina lightweight products technology and search for new alternative raw materials along with the currently used alumina grade S. The properties dependence of alumina lightweight products, obtained by the semi-dry pressing method, on the type of alumina α-form, was investigated.
 As a result of the studies, it was found that, for the manufacture of alumina lightweight products of grades KLA-1.1 and KLA-1.3 by the semi-dry pressing method, alumina grades N and NR can be used as an alternative alumina-containing raw material along with alumina grade S. The phase composition of alumina lightweight products of grades KLA-1.1 and KLA-1.3, which are manufactured using alumina grades S, N and NR, was represented mainly by corundum and calcium hexaluminate. The alumina lightweight products, which were manufactured using alumina grades S, N and NR, were characterized by similar high properties and correspond the technical requirements for grades KLA-1.1 and KLA-1.3.