Abstract

The relationships between the properties and structure are discussed for poly(vinyl alcohol)(PVA)/silica composites prepared through the sol-gel process. The composites became stiff and brittle with increasing the silica content. The properties of the composites were changed drastically at around the composition of PVA/silica = 70/30 wt %. For example, there was no large change in the Young's modulus above 30 wt % of silica content (Pure PVA: 31.8 MPa, silica 30%: 52.6 MPa, silica 50%: 55.2 MPa). Consequently, it was considered that the three-dimensional network structure of silica could be formed in the composite with more than 30 wt % of silica in PVA. From this behavior, it could be considered that the crystal growth of PVA was remarkably inhibited by silica network. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 74: 133–138, 1999